Breaking the conventional decrease of the Seebeck coefficient with increasing conductivity would be a significant advancement towards large thermoelectric power factor enhancement and high thermoelectric efficiency. We report on a mechanism identified in hyper-doped nanocrystalline Si films that can lead to this task: a transition from dominant ionized impurity scattering to dominant phonon scattering upon thermal annealing at a high annealing temperature T a that takes place to fulfill charge neutrality. We show that the synergy between charge neutrality and energy filtering activated by thermal annealing of the originally defective nanocrystalline sample leads to high mobility, simultaneous increase of the conductivity and the Seebeck coefficient and large enhancement of the thermoelectric power factor. This is demonstrated by means of advanced theoretical modeling and excellent quantitative agreement with the experiment. Our work provides interpretation of so far not understood observations in nanocrystalline Si and indicates a new route for engineering Si as well as other nanostructured materials for high thermoelectric efficiency.

Zianni, X., Narducci, D. (2019). Synergy between defects, charge neutrality and energy filtering in hyper-doped nanocrystalline materials for high thermoelectric efficiency. NANOSCALE, 11(16), 7667-7673 [10.1039/c8nr09263j].

Synergy between defects, charge neutrality and energy filtering in hyper-doped nanocrystalline materials for high thermoelectric efficiency

Narducci, D
2019

Abstract

Breaking the conventional decrease of the Seebeck coefficient with increasing conductivity would be a significant advancement towards large thermoelectric power factor enhancement and high thermoelectric efficiency. We report on a mechanism identified in hyper-doped nanocrystalline Si films that can lead to this task: a transition from dominant ionized impurity scattering to dominant phonon scattering upon thermal annealing at a high annealing temperature T a that takes place to fulfill charge neutrality. We show that the synergy between charge neutrality and energy filtering activated by thermal annealing of the originally defective nanocrystalline sample leads to high mobility, simultaneous increase of the conductivity and the Seebeck coefficient and large enhancement of the thermoelectric power factor. This is demonstrated by means of advanced theoretical modeling and excellent quantitative agreement with the experiment. Our work provides interpretation of so far not understood observations in nanocrystalline Si and indicates a new route for engineering Si as well as other nanostructured materials for high thermoelectric efficiency.
Articolo in rivista - Articolo scientifico
Silicon, Thermoelectricity, Energy Filtering
English
2019
11
16
7667
7673
partially_open
Zianni, X., Narducci, D. (2019). Synergy between defects, charge neutrality and energy filtering in hyper-doped nanocrystalline materials for high thermoelectric efficiency. NANOSCALE, 11(16), 7667-7673 [10.1039/c8nr09263j].
File in questo prodotto:
File Dimensione Formato  
manuscript-revised (post-print).pdf

accesso aperto

Tipologia di allegato: Author’s Accepted Manuscript, AAM (Post-print)
Dimensione 807.64 kB
Formato Adobe PDF
807.64 kB Adobe PDF Visualizza/Apri
Synergy between defects, charge neutrality and energy filtering in hyper-doped nanocrystalline materials for high thermoelectric efficiency.pdf

Solo gestori archivio

Tipologia di allegato: Publisher’s Version (Version of Record, VoR)
Dimensione 1.09 MB
Formato Adobe PDF
1.09 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/238272
Citazioni
  • Scopus 17
  • ???jsp.display-item.citation.isi??? 17
Social impact