Multifunctional role of rare earth doping in optical materials: Nonaqueous sol-gel synthesis of stabilized cubic HfO2 luminescent nanoparticles

In this work a strategy for the control of structure and optical properties of inorganic luminescent oxide-based nanoparticles is presented. The nonaqueous sol-gel route is found to be suitable for the synthesis of hafnia nanoparticles and their doping with rare earths (RE) ions, which gives rise to their luminescence either under UV and X-ray irradiation. Moreover, we have revealed the capability of the technique to achieve the low-temperature stabilization of the cubic phase through the effective incorporation of trivalent RE ions into the crystal lattice. Particular attention has been paid to doping with europium, causing a red luminescence, and with lutetium. Structure and morphology characterization by XRD, TEM/SEM, elemental analysis, and Raman/IR vibrational spectroscopies have confirmed the occurrence of the HfO2 cubic polymorph for dopant concentrations exceeding a threshold value of nominal 5 mol %, for either Lu3+ or Eu3+. The optical properties of the nanopowders were investigated by room temperature radio- and photoluminescence experiments. Specific features of Eu3+ luminescence sensitive to the local crystal field were employed for probing the lattice modifications at the atomic scale. Moreover, we detected an intrinsic blue emission, allowing for a luminescence color switch depending on excitation wavelength in the UV region. We also demonstrate the possibility of changing the emission spectrum by multiple RE doping in minor concentration, while deputing the cubic phase stabilization to a larger concentration of optically inactive Lu3+ ions. The peculiar properties arising from the solvothermal nonaqueous synthesis here used are described through the comparison with thermally treated powders. © 2013 American Chemical Society.