Highly selective membranes with controlled porosity can be obtained by growing thin films of mesoporous oxides on an appropriate support. This can be achieved employing organic/inorganic mixed micellar solutions based on metal oxide precursors and commercial templates. In particular amphiphilic block copolymers are very attractive materials as soft-templating agents because they self-assemble into micelles whose morphology and size depend on block composition and solution parameters. Large-mesopore silica films with narrow pore size distribution and high porosity have been obtained by sol–gel reaction of a silicon oxide precursor (TEOS) and using polystyrene-block-poly(ethylene-oxide) (PS-b-PEO) copolymers as templates. In order to modulate size, shape and alignment of the pores, many variables were changed: block copolymer chain length, TEOS/block copolymer ratio, solvent ratio, additives (i.e. polystyrene homopolymer addition). The effect of the different parameters on the porous system was studied by microscopy techniques and gas-volumetric analyses. Final aim of this work is the preparation of silica membranes to be used as selective gates for controlled dosing and transport of chemical species in solution.

Nistico', R., Scalarone, D., Magnacca, G. (2014). Preparation and physico-chemical characterization of large-mesopore silica thin films templated by block copolymers for membrane technology. MICROPOROUS AND MESOPOROUS MATERIALS, 190, 208-214 [10.1016/j.micromeso.2014.02.012].

Preparation and physico-chemical characterization of large-mesopore silica thin films templated by block copolymers for membrane technology

NISTICO', ROBERTO
Primo
;
2014

Abstract

Highly selective membranes with controlled porosity can be obtained by growing thin films of mesoporous oxides on an appropriate support. This can be achieved employing organic/inorganic mixed micellar solutions based on metal oxide precursors and commercial templates. In particular amphiphilic block copolymers are very attractive materials as soft-templating agents because they self-assemble into micelles whose morphology and size depend on block composition and solution parameters. Large-mesopore silica films with narrow pore size distribution and high porosity have been obtained by sol–gel reaction of a silicon oxide precursor (TEOS) and using polystyrene-block-poly(ethylene-oxide) (PS-b-PEO) copolymers as templates. In order to modulate size, shape and alignment of the pores, many variables were changed: block copolymer chain length, TEOS/block copolymer ratio, solvent ratio, additives (i.e. polystyrene homopolymer addition). The effect of the different parameters on the porous system was studied by microscopy techniques and gas-volumetric analyses. Final aim of this work is the preparation of silica membranes to be used as selective gates for controlled dosing and transport of chemical species in solution.
Articolo in rivista - Articolo scientifico
Block copolymers; Mesoporous silica; Soft-templating; Sol–gel synthesis; Membranes;
English
208
214
7
Nistico', R., Scalarone, D., Magnacca, G. (2014). Preparation and physico-chemical characterization of large-mesopore silica thin films templated by block copolymers for membrane technology. MICROPOROUS AND MESOPOROUS MATERIALS, 190, 208-214 [10.1016/j.micromeso.2014.02.012].
File in questo prodotto:
File Dimensione Formato  
2014_Nisticò_MicropMesopMater.pdf

Solo gestori archivio

Descrizione: Articolo principale
Tipologia di allegato: Publisher’s Version (Version of Record, VoR)
Dimensione 2.43 MB
Formato Adobe PDF
2.43 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/349608
Citazioni
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 18
Social impact