Magnetite nanoparticles (NPs) were synthetized by partial oxidation of hot Fe(II) sulfate aqueous solutions upon addition of variable amounts of alkali/nitrate ions in a N2 atmosphere. The resulting NPs were extensively characterized by Scanning Electron Microscopy (SEM), X-Ray Powder Diffraction (XRPD), Dynamic Light Scattering (DLS) and Brunauer-Emmett-Teller (BET) analysis. Depending on the final pH after synthesis, partially oxidized magnetite NPs were obtained with average crystallite size ranging from 29 to 116 nm. The potential of NPs as arsenic adsorbents was investigated through batch adsorption experiments. The analysis of the adsorption isotherms performed on the basis of both Freundlich and Langmuir models, revealed that arsenic adsorption capacity was more efficient for magnetite NPs synthetized at final pH ≤ 6.56, characterized by polydisperse submicrometric aggregates with coarse macro- and mesopore distributions.
Di Iorio, E., Colombo, C., Cheng, Z., Capitani, G., Mele, D., Ventruti, G., et al. (2019). Characterization of magnetite nanoparticles synthetized from Fe(II)/nitrate solutions for arsenic removal from water. JOURNAL OF ENVIRONMENTAL CHEMICAL ENGINEERING, 7(2) [10.1016/j.jece.2019.102986].
Characterization of magnetite nanoparticles synthetized from Fe(II)/nitrate solutions for arsenic removal from water
Capitani, GMembro del Collaboration Group
;
2019
Abstract
Magnetite nanoparticles (NPs) were synthetized by partial oxidation of hot Fe(II) sulfate aqueous solutions upon addition of variable amounts of alkali/nitrate ions in a N2 atmosphere. The resulting NPs were extensively characterized by Scanning Electron Microscopy (SEM), X-Ray Powder Diffraction (XRPD), Dynamic Light Scattering (DLS) and Brunauer-Emmett-Teller (BET) analysis. Depending on the final pH after synthesis, partially oxidized magnetite NPs were obtained with average crystallite size ranging from 29 to 116 nm. The potential of NPs as arsenic adsorbents was investigated through batch adsorption experiments. The analysis of the adsorption isotherms performed on the basis of both Freundlich and Langmuir models, revealed that arsenic adsorption capacity was more efficient for magnetite NPs synthetized at final pH ≤ 6.56, characterized by polydisperse submicrometric aggregates with coarse macro- and mesopore distributions.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.