Due to easiness of preparation and high energy density, V2O 5 nanocrystalline thin films are particularly attractive as cathode materials for all-solid-state rechargeable lithium microbatteries. However, their electrochemical performances are strictly related to the film microstructure, which, in turn, is related to the nature and parameters of the deposition technique. For this reason, the preparation of thin films with reproducible electrochemical properties is still an open problem. Here, we report on the deposition of V2O5 crystalline thin films by means of reactive radiofrequency (r.f.) magnetron sputtering, using vanadium metal as the target. Different deposition times and substrate temperatures were adopted. X-ray powder diffraction (XRD) and atomic force microscopy were used to investigate the structural and morphological features of the films. In particular, XRD analysis revealed that the deposition parameters affect the crystallographic orientation of the films. A h 0 0 orientation is observed in case of thin samples (about 100 nm) prepared at 300 °C, whereas a 1 1 0 preferential growth is obtained for thicker films. Films deposited at 500 °C display a 0 0 1 orientation irrespective on the deposition time. Reversible Li intercalation/deintercalation processes and high specific capacity are observed for the h 0 0-oriented V2O5 thinner films, with the ab plane arranged perpendicular to the substrate. In this case, the cycling behaviour is very promising, and a stable capacity higher than 300 mAh g -1 was delivered in the potential range 3.8-1.5 V at 1C rate over at least 70 cycles

Quinzeni, I., Ferrari, S., Quartarone, E., Mustarelli, P. (2011). Structural, morphological and electrochemical properties of nanocrystalline V2O5 thin films deposited by means of r.f magnetron sputtering. JOURNAL OF POWER SOURCES, 196(23), 10228-10233 [10.1016/j.jpowsour.2011.08.073].

Structural, morphological and electrochemical properties of nanocrystalline V2O5 thin films deposited by means of r.f magnetron sputtering

Mustarelli, P
2011

Abstract

Due to easiness of preparation and high energy density, V2O 5 nanocrystalline thin films are particularly attractive as cathode materials for all-solid-state rechargeable lithium microbatteries. However, their electrochemical performances are strictly related to the film microstructure, which, in turn, is related to the nature and parameters of the deposition technique. For this reason, the preparation of thin films with reproducible electrochemical properties is still an open problem. Here, we report on the deposition of V2O5 crystalline thin films by means of reactive radiofrequency (r.f.) magnetron sputtering, using vanadium metal as the target. Different deposition times and substrate temperatures were adopted. X-ray powder diffraction (XRD) and atomic force microscopy were used to investigate the structural and morphological features of the films. In particular, XRD analysis revealed that the deposition parameters affect the crystallographic orientation of the films. A h 0 0 orientation is observed in case of thin samples (about 100 nm) prepared at 300 °C, whereas a 1 1 0 preferential growth is obtained for thicker films. Films deposited at 500 °C display a 0 0 1 orientation irrespective on the deposition time. Reversible Li intercalation/deintercalation processes and high specific capacity are observed for the h 0 0-oriented V2O5 thinner films, with the ab plane arranged perpendicular to the substrate. In this case, the cycling behaviour is very promising, and a stable capacity higher than 300 mAh g -1 was delivered in the potential range 3.8-1.5 V at 1C rate over at least 70 cycles
Articolo in rivista - Articolo scientifico
RF sputtering, thin films, cathode
English
2011
196
23
10228
10233
none
Quinzeni, I., Ferrari, S., Quartarone, E., Mustarelli, P. (2011). Structural, morphological and electrochemical properties of nanocrystalline V2O5 thin films deposited by means of r.f magnetron sputtering. JOURNAL OF POWER SOURCES, 196(23), 10228-10233 [10.1016/j.jpowsour.2011.08.073].
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/256967
Citazioni
  • Scopus 34
  • ???jsp.display-item.citation.isi??? 30
Social impact