Borosilicate materials are of interest for many technological applications. Whereas sol-gel techniques are well suited for the preparation of these materials, the nominal concentration of boron is often not maintained, and a considerable amount of boron is lost during the preparation procedure. In this work we deal with the synthesis of borosilicate systems in order to analyse the problem of the boron loss. Different sol-gel precursors of B 2O 3 were explored and organically modified silicon alcoxide were tested, in addition P 2O 5 co-doping was proposed. IR spectroscopy, differential Scanning Calorimetry, Thermogravimetry and ICP-OES analyses were performed. Sol-gel synthesis of SiO 2-B 2O 3 xerogels with a high boron content (> 18 wt.%) was successfully obtained by employing trimethoxyboroxine and 3- aminopropyltriethoxysilane

Grandi, S., Tomasi, C., Cassinelli, V., Cucca, L., Profumo, A., Mustarelli, P., et al. (2012). SiO 2-B 2O 3 xerogels: The problem of boron leaching. JOURNAL OF NON-CRYSTALLINE SOLIDS, 358(14), 1631-1637 [10.1016/j.jnoncrysol.2012.04.025].

SiO 2-B 2O 3 xerogels: The problem of boron leaching

Mustarelli, P;
2012

Abstract

Borosilicate materials are of interest for many technological applications. Whereas sol-gel techniques are well suited for the preparation of these materials, the nominal concentration of boron is often not maintained, and a considerable amount of boron is lost during the preparation procedure. In this work we deal with the synthesis of borosilicate systems in order to analyse the problem of the boron loss. Different sol-gel precursors of B 2O 3 were explored and organically modified silicon alcoxide were tested, in addition P 2O 5 co-doping was proposed. IR spectroscopy, differential Scanning Calorimetry, Thermogravimetry and ICP-OES analyses were performed. Sol-gel synthesis of SiO 2-B 2O 3 xerogels with a high boron content (> 18 wt.%) was successfully obtained by employing trimethoxyboroxine and 3- aminopropyltriethoxysilane
Articolo in rivista - Articolo scientifico
BNCT, nanoparticles
English
2012
358
14
1631
1637
none
Grandi, S., Tomasi, C., Cassinelli, V., Cucca, L., Profumo, A., Mustarelli, P., et al. (2012). SiO 2-B 2O 3 xerogels: The problem of boron leaching. JOURNAL OF NON-CRYSTALLINE SOLIDS, 358(14), 1631-1637 [10.1016/j.jnoncrysol.2012.04.025].
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/256959
Citazioni
  • Scopus 7
  • ???jsp.display-item.citation.isi??? 6
Social impact