The analysis of the photoluminescence (PL) spectra of a number of silicon samples plastically deformed or simply thermally annealed was used to understand the role of oxygen and oxygen precipitates on the PL emissions in the 0.8-1.0 eV range. The results of this analysis show that it is possible to discriminate between emissions due to oxygen-associated centres and those due to dislocations. Furthermore, it has been shown on a sample presenting only (dissociated) 60° dislocations that the 0.807 eV emission is absent, demonstrating that it comes either from dislocation intersections or from screw segments. Finally, it has been suggested that the strain field associated to oxide precipitates might be responsible of both narrow and broad bands, systematically present in most of the samples examined, which are therefore interpreted as being due to carrier confinement effects in localized quantum wells at silicon/silicon oxide interfaces of oxide precipitates.

Pizzini, S., Leoni, E., Binetti, S., Acciarri, M., LE DONNE, A., Pichaud, B. (2004). Luminescence of Dislocations and Oxide Precipitates in Si. DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA, 95-96, 273-282 [10.4028/www.scientific.net/SSP.95-96.273].

Luminescence of Dislocations and Oxide Precipitates in Si

Pizzini, S;BINETTI, SIMONA OLGA;ACCIARRI, MAURIZIO FILIPPO;LE DONNE, ALESSIA;
2004

Abstract

The analysis of the photoluminescence (PL) spectra of a number of silicon samples plastically deformed or simply thermally annealed was used to understand the role of oxygen and oxygen precipitates on the PL emissions in the 0.8-1.0 eV range. The results of this analysis show that it is possible to discriminate between emissions due to oxygen-associated centres and those due to dislocations. Furthermore, it has been shown on a sample presenting only (dissociated) 60° dislocations that the 0.807 eV emission is absent, demonstrating that it comes either from dislocation intersections or from screw segments. Finally, it has been suggested that the strain field associated to oxide precipitates might be responsible of both narrow and broad bands, systematically present in most of the samples examined, which are therefore interpreted as being due to carrier confinement effects in localized quantum wells at silicon/silicon oxide interfaces of oxide precipitates.
Articolo in rivista - Articolo scientifico
Annealing; Crystal defects; Dislocations (crystals); Electron diffraction; Fourier transform infrared spectroscopy; Monochromators; Nucleation; Oxygen; Photoluminescence; Plastic deformation; Precipitation (chemical); Semiconductor quantum wells; Transmission electron microscopy, Bulk microdefect density (BMD); Localized quantum wells; X-ray topography (XRT), Silicon
English
2004
95-96
273
282
none
Pizzini, S., Leoni, E., Binetti, S., Acciarri, M., LE DONNE, A., Pichaud, B. (2004). Luminescence of Dislocations and Oxide Precipitates in Si. DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA, 95-96, 273-282 [10.4028/www.scientific.net/SSP.95-96.273].
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10281/23852
Citazioni
  • Scopus 34
  • ???jsp.display-item.citation.isi??? 30
Social impact